The alloys have the following advantages :
- Obtain Uniform Shade and Shine in Jewellery Manufactured by Different Kari-gars.
- Reduce production losses and save 0.3% to 1% Gold.
- Consistent color in White, Pink, Yellow, and Red.
- Increase productivity.
- Reduce defects.
- Better finish.
Products List
| Type of Work | Karatage | Recommended Alloys | Silver Content | Special Features | Brochure |
|---|---|---|---|---|---|
| Casting | 22/18 | 1210 | 44% | Best casting quality. Ideal for casting with stones (22 and 18 Kt) due to low melting and casting temperature. Strongly recommended for 18 Kt bangles. Offers higher flexibility. Can be used for 18 Kt stamping and mechanical work. Equivalent to 394, 790, 860. |
Download(18KT)
Download(22KT) |
| 1209 | 18% | Ideal for casting of 22 kt. Lower cost than 1210. |
Download(18KT)
Download(22KT) |
||
| 22 | 1201 | 5% | More affordable than 1210. 1210 gives a better finish but 1201 offers flexibility of usage. 1201 can also be used for hand making and chains. |
Download | |
| 22/18 | 1212 | 23% | Ideal for casting with stones . Mechanical working. |
Download(22KT)
Download(18KT) |
|
| Chain Making | 22/18 | 1208 | 40% | Can be drawn up to 0.2 mm after annealing at 60%. can be used for section and wire below 0.3mm. Equivalent to 394, 801. |
Download(22KT)
Download(18KT) |
| 22 | 1201 | 5% | Lower cost than 1208, Harder to work with than 1208. Not recommended be used for a thin section or wires below 0.3mm. |
Download | |
| Mechanical and Stamping | 22 | 1208 | 40% | Better malleability than 1201, Not recommended for casting. | Download(22KT) |
| 1201 | 5% | Can be used for casting and mechanical work. Lower cost than 1208. |
Download |
Today's Alloys Rates ( Suggested Price Including GST )
Note: The above prices are indicative only and Ex- works, Bangalore. Additional charges may be applicable as per the location.
| Type of Work | Karatage | Recommended Alloys | Silver Content | Special Features | Brochure |
|---|---|---|---|---|---|
| Casting Rose Gold | 22 /18 kt | 1202 | 3% | Fine Casting. Can be also used for Handwork and Mechanical. |
Download(18KT)
Download(22KT) |
| Mechanical & Stamping | 22/18 kt | 1211 | 3% | Ideal for Mechanical. |
Download(18KT)
Download(22KT) |
Today's Alloys Rates ( Suggested Price Including GST )
Note: The above prices are indicative only and Ex- works, Bangalore. Additional charges may be applicable as per the location.
| Type of Work | Karatage | Recommended Alloys | Silver Content | Special Features | Brochure |
|---|---|---|---|---|---|
| Mechanical & Stamping | 18 | 1205 | 0% | Ideal White Alloy for Mechanical work and stamping. Equivalent to 866. | Download(14KT) Download(18KT) |
Today's Alloys Rates ( Suggested Price Including GST )
Note: The above prices are indicative only and Ex- works, Bangalore. Additional charges may be applicable as per the location.
MASTER ALLOY CONSOLIDATED DATA
Last updated 25-12-2019
| Sr No | Alloy | Ag % | Color | L* | a* | b* | Melting Temp C | Casting Temp C | Flask Temp C | Annealing Temp C | Cast Hardness(HV) | Anneal Hardness(HV) | Hardness after 50%(HV) | Tensile Strength N/sqmm | Yield Strength N/sqmm | Elonga-tion % | Stone In Place Casting | Machine Made | Hand made | Chain | Induction Melting | Casting | Fabrication | Wire | Stamping | Soldering | Continous Casting |
22Kt |
|||||||||||||||||||||||||||
| 1 | YC1202 | 4 | Pinkish Yellow | 87.8 | 14.98 | 34.02 | 990 | 1040 | 600 | 550 | 98.71 | 88.63 | 165.5 | 312.027 | 144.535 | 46 | Y | Y | Y | Y | Y | Y | Y | Y | Y | Y | |
| 3 | YM1208 | 40 | Deep Yellow | 87.38 | 10.2 | 39.34 | 900 | N/A | N/A | 500 | 105.56 | 70.07 | 151.53 | 288.773 | 122.661 | 44.5 | Y | Y | Y | Y | Y | Y | Y | Y | |||
| 4 | YC1210 | 44 | Yellow | 88.74 | 10.8 | 40.26 | 980 | 1030 | 600 | 500 | 105.56 | 70.07 | 151.53 | 286.65 | 114.38 | 43.5 | Y | Y | Y | Y | Y | Y | Y | ||||
| 5 | YG1209 | 18 | Yellow | 88.88 | 12.88 | 33.54 | 930 | 1025 | 600 | 500 | 110.83 | 85.63 | 164.03 | 327.961 | 151.916 | 49.9 | Y | Y | Y | Y | Y | Y | Y | Y | |||
| 6 | YC1212 | 24 | Yellow | 87.14 | 13.4 | 35.04 | 920 | 1010 | 600 | 550 | 103.83 | 81.72 | 151.56 | 324.863 | 137.421 | 53.2 | Y | Y | Y | Y | Y | Y | Y | Y | |||
| 7 | PG1204 | 3 | Dark Rose | 87.92 | 13.52 | 31.92 | 980 | 1035 | 600 | 550 | 118 | 85 | 160 | Y | |||||||||||||
| 8 | WC1206 | Reddish | Y | Y | Y | Y | Y |
| Sr No | Alloy | Ag % | Color | L* | a* | b* | Melting Temp C | Casting Temp C | Flask Temp C | Annealing Temp C | Cast Hardness(HV) | Anneal Hardness(HV) | Hardness after 50%(HV) | Tensile Strength N/sqmm | Yield Strength N/sqmm | Elonga-tion % | Stone In Place Casting | Machine Made | Hand made | Chain | Induction Melting | Casting | Fabrication | Wire | Stamping | Soldering | Continous Casting |
18Kt |
|||||||||||||||||||||||||||
| 1 | YC1202 | 4 | Pink | 87.2 | 13.04 | 19.56 | 990 | 1040 | 600 | 550 | 158.16 | 149.16 | 256.4 | 480.521 | 309.516 | 44.1 | Y | Y | Y | Y | Y | Y | Y | Y | Y | Y | |
| 2 | WC1205 | Off White | 87.26 | 5.38 | 15.46 | 985 | 1030 | 600 | 660 | 172.4 | 170.66 | 271.56 | 542.927 | 386.092 | 41 | Y | Y | Y | Y | Y | Y | Y | Y | Y | |||
| 3 | YG1209 | 18 | Yellow | 88.06 | 29.36 | 64.34 | 920 | 1010 | 600 | 500 | 177 | 175.7 | 244.8 | 525.375 | 357.769 | 52.3 | Y | Y | Y | Y | Y | Y | Y | Y | |||
| 4 | YC1210 | 44 | Yellow | 97.46 | 2.12 | 35.42 | 990 | 1035 | 600 | 500 | 166 | 150.83 | 224.4 | 485.686 | 312.843 | 59.9 | Y | Y | Y | Y | Y | Y | Y | ||||
| 6 | YM1208 | 40 | Deep Yellow | 90.32 | 10.58 | 25.46 | 850 | N/A | N/A | 550 | 180.55 | 155.2 | 234.5 | 507.367 | 331.908 | 30.9 | Y | Y | Y | Y | Y | Y | Y | Y | |||
| 7 | WC1206 | Reddish | Y | Y | Y | Y | Y | Y | Y | Y | Y | ||||||||||||||||
| 8 | PG1204 | 3 | Dark Rose | 81.3 | 12.72 | 25.04 | 980 | 1035 | 600 | 550 | 201 | 125 | 260 | Y | |||||||||||||
| 9 | YC1212 | 24 | Yellow | 89.1 | 11.2 | 24.6 | 910 | 1005 | 600 | 550 | 168.3 | 165 | 238.56 | 495.336 | 322.378 | 76.9 | Y | Y | Y | Y | Y | Y | Y | Y | |||
| 10 | PG1211 | 6.4 | Rose Gold | 980 | 1035 | 600 | 600 | Y | Y | Y | Y | Y |
| Sr No | Alloy | Ag % | Color | L* | a* | b* | Melting Temp C | Casting Temp C | Flask Temp C | Annealing Temp C | Cast Hardness(HV) | Anneal Hardness(HV) | Hardness after 50%(HV) | Tensile Strength N/sqmm | Yield Strength N/sqmm | Elonga-tion % | Stone In Place Casting | Machine Made | Hand made | Chain | Induction Melting | Casting | Fabrication | Wire | Stamping | Soldering | Continous Casting |
14Kt |
|||||||||||||||||||||||||||
| 1 | WC1205 | Off White | 86.22 | 4.3 | 13.7 | 970 | 1020 | 600 | 650 | 176.76 | 158.83 | 279.16 | 579.848 | 350.184 | 38.1 | Y | Y | Y | Y | Y | Y | Y | Y | Y | |||
| 2 | PG1211 | 6.4 | Rose Gold | 88.5 | 13 | 18 | 980 | 1035 | 600 | 600 | 158.2 | 138.8 | 219.4 | 523.124 | 296.648 | 49.5 | Y | Y | Y | Y | Y | ||||||
| 3 | YC1210 | 40 | Yellow | 89.54 | 9.6 | 24.12 | 960 | 1010 | 600 | 550 | 192.1 | 181.3 | 252.3 | Y | Y | Y | Y | Y | Y | Y | |||||||
| 4 | WC1206 | Off White | Y | Y | Y | Y | Y | Y | Y | Y | Y | ||||||||||||||||